Audited Supplier ASTM A312 S30815 (253MA, 1.4835) Stainless Steel Seamless Pipe
ASTM A312 S30815 (253MA, 1.4835) Stainless Steel Seamless Pipe
253MA is an austenitic stainless steel with excellent high-temperature resistance. It is composed of chromium, nickel, molybdenum, and nitrogen with excellent corrosion resistance, and added with trace amounts of rare earth metal elements to improve its oxidation resistance and high-temperature strength.Hardness and melting point 253MA has a high hardness and melting point. Its hardness is 170-220HBW (Brinell hardness) and its melting point is 1370-1425 ºC.
253MA is a high-temperature alloy with excellent high-temperature resistance. It can be used for a long time at temperatures up to 1150 ºC, and can still maintain good mechanical and antioxidant properties at high temperatures.The elastic modulus and Poisson's ratio of 253MA are 200 GPa and Poisson's ratio is 0.3.The density of 253MA is 7.8 g/cm ³.Standard 253MA complies with ASTM A240, A276, A312, A479, and A813 standards.The yield strength of 253MA is ≥ 310 MPa, tensile strength is ≥ 600 MPa, and elongation is ≥ 30%.
253MA has excellent mechanical properties and can maintain stable mechanical properties in high temperature and corrosive environments.
Characteristic 253MA not only has good high-temperature resistance, but also has good corrosion resistance and antioxidant performance. In corrosive environments containing sulfuric acid and other strong acids, 253MA can still maintain excellent corrosion resistance. In addition, 253MA also has good heat shock resistance and thermal stability.Overall, 253MA is an excellent high-temperature alloy material with excellent high-temperature strength, oxidation resistance, and corrosion resistance. Due to its widespread application in furnaces, heating equipment, heat exchangers, and other high-temperature equipment, 253MA is a very useful material for applications that can withstand high temperatures and corrosive environments
S30815 is a heat-resistant austenitic stainless steel with high creep strength and good corrosion resistance, suitable for applications requiring high creep strength and good corrosion resistance, such as sintering equipment, blast furnace equipment, steel melting, furnaces and continuous casting equipment, rolling machines (heating furnaces), heat treatment furnaces and accessories, mineral equipment and cement production equipment
chemical composition of 253MA
| Chromium | Nickel | Rare earth elements | Molybdenum | Manganese | Silicon | Nitrogen | Carbon | Phosphorus | Sulfur |
| 20.0-22.0% | 10.0-12.0% | 0.03-0.08% | 1.8-2.5% | 0.80-1.50% | 1.40-2.00% | 0.14-0.20% | ≤ 0.05% | ≤ 0.04% | ≤ 0.03% |
253 MA Mechanical Property
| Grade | TensileStrength(MPa) min | YieldStrength 0.2% Proof (MPa) min |
Elongation (% in 50mm) min | Hardness | |
| RockwellB (HR B) max |
Brinell (HB) max | ||||
| 253MA | 600 | 310 | 40 | 95 | 217 |
253 MA Physical Propertie
| Grade | Density (kg/m3) | Elastic Modulus (GPa) | Mean Coefficient of Thermal Expansion (mm/m/°C) | Thermal Conductivity (W/m.K) | Specific Heat 0-100°C (J/kg.K) |
Electrical Resistivity (nW.m) | |||
| 0-100°C | 0-600°C | 0-1000°C | at 20°C | at 1000°C | |||||
| 253MA | 7800 | 200 | 17.0 | 18.5 | 19.5 | 15.0 | 29.0 | 500 | 850 |