| Customization: | Available |
|---|---|
| After-sales Service: | Supplied |
| Warranty: | 30 Years |
|
Still deciding? Get samples of US$ 10/Piece
Request Sample
|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
| Material Grade: | Incoloy 800( NO8800,1.4876), 800H( NO8810, 1.4958), 800HT(NO8811,1.4959), | Standard: | ASTM B407, ASME SB407, ASTM A213, ASME SA213 , ASTM A312, ASME SA312 |
|---|---|---|---|
| NDT: | PT, UT, ET, HT | Type: | Welded Pipe, Welded Tube, Seamless Pipe, Seamless Tube |
| High Light: |
nickel alloy tube,hastelloy c tubing |
||
Nickel Alloy Pipe, ASTM B407 Incoloy 800( NO8800,1.4876), 800H( NO8810, 1.4958), 800HT(NO8811,1.4959)
| Trade Name | INCOLOY® 800 | INCOLOY® 800H | INCOLOY® 800HT | INCOLOY® 825 |
| UNS # | N08800 | N08810 | N08811 | N08825 |
| Seamless Pipe / Tube | B/SB407 | B/SB407 | B/SB407 | B/SB423 |
| A/SA312 | A/SA312 | A/SA312 | B/SB163 | |
| B/SB163 | B/SB163 | B/SB163 | ||
| A/SA213 | A/SA213 | A/SA213 | ||
| Welded Pipe / Tube | B/SB515 | B/SB515 | B/SB515 | B/SB705 |
| B/SB514 | B/SB514 | A/SA312 | B474 | |
| A/SA312/ | A/SA312/ | B/SB704 | ||
| A/SA358 | A/SA358 | |||
| Buttweld Fittings* | B/SB366 | B/SB366 | B/SB366 | B/SB366 |
| Grade | Grade | Grade | Grade | |
| WPNIC | WPNIC10 | WPNIC11 | WPNICMC | |
| Forged Valves | B/SB564 | B/SB564 | B/SB564 | B/SB564 |
| B/SB425 BAR | ||||
| Forged Fittings | B/SB564 | B/SB564 | B/SB564 | B/SB564 |
| Flanges | B/SB564 | B/SB564 | B/SB564 | B/SB564 |
| Plate | B/SB409 | B/SB409 | B/SB409 | B/SB424 |
| A/SA240 | A/SA240 | A/SA240 | ||
| Cast Steel Valves | A/SA351 | A/SA351 | ----- | A/SA494 |
| UNS N08151 | UNS N08151 | UNS N08826 | ||
| Grade | CT15C | CT15C | ----- | CU5MCuC |
Alloy 800, 800H, and 800HT are nickel-iron-chromium alloys with good strength and excellent resistance
to oxidation and carburization in high-temperature exposure. These nickel steel alloys are identical except
for the higher level of carbon in alloy 800H/HT and the addition of up to 1.20 percent aluminiumand
itanium in alloy 800HT. 800 was the first of these alloys and it was slightly modified into 800H. This
modification was to control carbon (.05-.10%) and grain size to optimize stress rupture properties.
In heat treatment applications 800HT has further modifications to the combined titanium and aluminium
levels (.85 - 1.20%) to ensure optimum high temperature properties.Alloy 800H/HT was intended for high
temperature structural applications. The nickel content makes the alloys highly resistant to both carborisation
and to embrittlement from precipitation of sigma phase.
Pipe and Tubes - ASTM B 163 & ASME SB 163 (Seamless Condenser & Heat Exchanger Tubes),
ASTM B 407/B 829 & ASME SB 407/SB 829 (Seamless Pipe & Tubes), ASTM B 514/B 775 &
ASME SB 514/SB 775 (Welded Pipe), ASTM B 515/B 751 & ASME SB 515/SB 751(Welded Tubes),
ASMECode Case 1325 (All Product Forms),ASME N-20 (Cold Worked SeamlessCondenser and
Heat Exchanger Tubes for Nuclear Service), BS 3074NA15 (Seamless Pipe & Tubes), SEW 470
(All Products), VdTÜV 412 (All Products), ISO 6207 (Seamless Tubing) Other Product Forms -
ASTM B 366 & ASME SB 366 (Fittings)