ASME Sb111 C7060 68700 Copper Pipe Polished Pipe

• Customization: Available
• Type: Copper Pipe
• Standard: ASTM, AISI, GB, JIS, DIN, EN
• Model NO.: Copper Pipe
• Grade: T1, T2, T3, C1100, C1010, H59, H58, etc.
• Certification: ISO, RoHS, IBR, AISI, ASTM, GB, EN, DIN, JIS
• Shape: Round/Customized
• Technique: Forged/ Hot Press
• Surface Treatment: Smooth/as Per Client′s Design
• Length: 10mm-12000mm
• Process: Bending, Decoiling, Welding, Punching, Cutting
• Diameter: 4mm, 6mm, 8mm, 10mm, 12mm, 15mm, 18mm, 22mm, 28mm,
• End: Plain End/Bevel End
• Test: BV, SGS Is Available
• Model Number: C44300
• Processing: Customized
• Wall Thickness: 1mm~220mm (Sch5X~Sch Xxs)
• Used: Factory, Decoration, Food
• Packing: Standard Sea Worthy Package
• Delivery Time: 10-30 Working Days
• MOQ: 1 Ton
• Application: Building, Sanitation, Seawater Desalination
• Technical: Hot Rolled/Cold Drawn
• Outside Diameter: 8mm, 10mm, 12mm, 15mm, 18mm, 28mm, 35mm, 42mm, etc
• Transport Package: Woven Bag/Wooden Case
• Specification: Brass/Copper
• Trademark: EZS
• Origin: China
• Production Capacity: 10000 Ton/Year

Product Description

 

Product Name	ASME SB111 C7060 68700 Coil Copper Pipe Polished Pipe
Size	Outside Diameter	2-914mm
	Thickness	1mm~220mm (Sch5X~Sch XXS)
	Max Length	1-50m
Surface	Polished,Yellow,Red
Process	Cold drawn, Hot Rolled
Usage	Gas Industry, Oilfield, Thermal power, Oil industry, Shipbuilding, Petrochemical, Tanker, Nuclear , etc
Surface	Pickling and annealing,pickling and annealing+polishing+ EP(Electricity polish)
End	Plain, Beveled with caps
Processing Service	Bending, Decoiling, Welding, Punching, Cutting
Certificate	ISO9001/2000
Standard	GB/T 19849-2005, EN 1254-1, ASTM B88M, BS EN1254, DIN 2856, etc.
Payment:	L/C at sight, L/C 180 days, T/T, D/P, OA, Western Union,
Port of Shipment	Shanghai port in China

Short Description:
This specification establishes the reguirements for seamless tube and ferrule stock of copper and various copper alloys of a specified range of diameters, for use in surface condensers, evaporators and heat exchangers.

The specified coppers and copper alloys are UNS No. C10100,C10200,C10300,C10800,C12000,C12200,C14200,C19200,C23000,C28000,C44300,C44400,
C44500,C60800,C61300,C61400,C68700,C70400,C70600,C70620,C71000,C71500, C71520,C71640 and C72200. The product shall be produced by processes such as casting, extrusion, drawing, annealing, straightening, trimming, and other processes which may produce a seamless tube in the specified condition. The coppers and copper alloys shall be specifically furnished in any one of the following tempers.: annealed, light-drawn, hard-drawn, or hard drawn and end annealed. Tubes for ferrule stock shall be annealed sufficiently to be fully crystallized.

Some tubes are suggested to be subjected to a stress-relieving thermal treatment subsequent to
straightening. The products shall be subjected to expansion, flattening, and residual stress tests
The tensile and expansion requirements for the products are specified in accordance with the
temper desianation. The products shall also be subjected to mercurous nitrate, ammonia vapor.
Eddy-current, hydrostatic, and pneumatic tests.

 

 

 

 

ASTM Standards:

• B153 Test Method for Expansion (Pin Test) of Copper and Copper-Alloy Pipe and Tubing.
• B154 Test Method for Mercurous Nitrate Test for Copper and Copper Alloys.
• B170 Specification for Oxygen-Free Electrolytic Copper Refinery Shapes.
• B224 Classification of Coppers.
• B846 Terminology for Copper and Copper Alloys.
• B858 Test Method for Ammonia Vapor Test for Determining Susceptibility to Stress Corrosion Cracking in Copper Alloys.
• E8 Test Methods for Tension Testing of Metallic Materials E 8M Test Methods for Tension Testing of Metallic Materials [Metric].
• E29 Practice for Using Significant Digits in Test Data to Determine Conformance with Specifications.
• E53 Test Methods for Determination of Copper in Unalloyed Coppers by Gravimetry.
• E54 Test Methods for Chemical Analysis of Special Brasses and Bronzes.
• E62 Test Methods for Chemical Analysis of Copper and Copper Alloys (Photometric Methods.
• E75 Test Methods for Chemical Analysis of Copper-Nickel and Copper-Nickel-Zinc Alloys.
• E76 Test Methods for Chemical Analysis of Nickel-Copper Alloys.
• E112 Test Methods for Determining Average Grain Size E 243 Practice for Electromagnetic (Eddy Current) Examination of Copper and Copper-Alloy Tubes.
• E255 Practice for Sampling Copper and Copper Alloys for the Determination of Chemical Composition.
• E478 Test Methods for Chemical Analysis of Copper Alloys.
• E527 Practice for Numbering Metals and Alloys (UNS).

Chemical Composition:

Designation	Chemical Composition %
	Cu	Sn	Al	As	Ni	Fe	Mn	Pb max.	Zn
C44300	70.0-73.0	0.9-1.2	-	0.02-0.06	-	0.06 max	-	0.07	Rem
C68700	76.0-79.0	-	1.8-2.5	0.02-0.06	-	0.06 max	-	0.07	Rem
C70400	Rem	-	-	-	4.8-6.2	1.3-1.7	0.3-0.8	0.05	1.0max
C70600	Rem	-	-	-	9.0-11.0	1.0-1.8	1.0max	0.05	1.0max
C71500	Rem	-	-	-	29.0-33.0	0.4-1.0	1.0max	0.05	1.0max
C71640	Rem	-	-	-	29.0-32.0	1.7-2.3	1.5-2.5	0.05	1.0max

 

The world standard Grade equivalent to ASTM B111

Material Designation	Corresponding Material Symbol
	GB/T8890	ASTM B111	BS2871	JIS H3300	DIN1785
Copper-Nickel	BFe10-1-1	C70600	CN102	C7060	CuNi10Fe1Mn
	BFe30-1-1	C71500	CN107	C7150	CuNi30Mn1Fe
	(BFe30-2-2)	C71640	CN108	C7164	CuNi30Fe2Mn2
	(BFe5-1.5-0.5)	C70400	-	-	-
	B7	-	-	-	-
Aluminums Brass	HAL77-2	C68700	CZ110	C6870	CuZn20Al2
Admiralty Brass	HSn70-1	C44300	CZ111	C4430	CuZn28Sn1
Boric Brass	Hsn70-18	-	-	-	-
	HSn70-1 AB	-	-	-	-
Arsenical Brass	H68A	-	CZ126	-	-
Brass Tube	H65/H63	C28000/C27200	CZ108	C2800/C2700	CuZn36/CuZn37

Tensile Requirements

Copper or Copper Alloy UNS NO.	Temper Designation		Tensile Strength	Yield Strength
	Standard	Former	min ksi	min ksi
C44300	O61	annealed	45	15
C68700	O61	annealed	50	18
C70400	H55	light-drawn	38	30
C70600	H55	light-drawn	45	15
C71500	O61	annealed	52	18
C71640	O61	annealed	63	25

 

Expansion Test

• Tube specimens selected for test shall withstand the expansion shown in standard when expanded in accordance with Test Method B 153. The expanded tube shall show no cracking or rupture visible to the unaided eye.
• Hard-drawn tubes not end annealed are not subject to this test. When tubes are specified end annealed, this test is required and shall be performed on the annealed ends of the sampled tubes.
• Tubes for ferrule stock are not subject to the expansion test.

Flattening Test

• Test Method-Each test specimen shall be flattened in a press at three (3) places along the length, each new place to be rotated on its axis approximately one third turn from the last flattened area. Each flattened area shall be at least 2 in. in length. A flattened test-specimen shall allow a micrometer caliper set at three (3) times the wall thickness to pass freely over the flattened area. The flattened areas of the test specimen shall be inspected for surface defects.
• During inspection, the flattened areas of the test- specimen shall be free of defects, but blemishes of a nature that do not interfere with the intended application are acceptable.
• Tubes for ferrule stock are not subject to flattening test.

Residual Stress Test

• A residual stress test is required to be performed only for Copper Alloy UNS Nos. C23000, C28000, C44300, C44400, C44500, C60800, C61300, C61400, and C68700.
• Unless otherwise specified, the producer shall have the option of testing the product to either the mercurous nitrate test, Test Method B 154, or the ammonia vapor test, Test Method B 858, as prescribed below.

Nondestructive Testing

Eddy-Current Test-Each tube shall be passed through an eddy-current testing unit adjusted to provide information on the suitability of the tube for the intended application. Testing shall follow the procedures of Practice E 243.

Hydrostatic Test

Each tube shall stand, without showing evidence of leakage, an internal hydrostatic pressure sufficient to subject the material to a fiber stress of 7000 psi [48 MPa] as determined by the following equation for thin hollow cylinders under tension. The tube need not be tested at a hydrostatic pressure of over 1000 psi [7.0 MPa] unless so specified.

 